Publicación: Influência da Baixa Temperatura de Recozimento na Evolução da Microestrutura da Liga Ni53Ti47 com Memória de Forma
Cargando...
Fecha
2024-10-22
Editor/a
Director/a
Tutor/a
Coordinador/a
Prologuista
Revisor/a
Ilustrador/a
Derechos de acceso
info:eu-repo/semantics/openAccess
Título de la revista
ISSN de la revista
Título del volumen
Editor
Universidad Nacional de Educación a Distancia (España), Universidad de Concepción - Chile. Departamento de Ingeniería Mecánica.
Resumen
As ligas NiTi quase equiatômicas (ou Nitinol) apresentam comportamento de memória de forma, superelasticidade, alta resistência, excelente resistência à corrosão e biocompatibilidade. Uma amostra experimental de liga NiTi foi submetida a recozimento em diferentes temperaturas, variando de 350°C a 650°C. Foram estudadas as propriedades microestruturais, térmicas e mecânicas antes e depois do tratamento térmico. A influência do tratamento térmico de recozimento em baixas temperaturas na microestrutura do Ni53Ti47 foi investigada. Os resultados mostraram que o tratamento de recozimento levou a mudanças na morfologia da microestrutura. Além disso, as temperaturas de transformação martensítica Ms e Af tendem a aumentar com o aumento da temperatura de recozimento. A fase R é apresentada nos corpos de prova considerando a faixa de 350°C a 550°C, com solubilização completa a 650°C. Estas alterações foram acompanhadas por uma diminuição gradual da dureza e um aumento do tamanho do grão com o aumento da temperatura de recozimento.
Near-equiatomic NiTi alloys (or Nitinol) exhibit shape memory behavior, superelasticity, high strength, excellent corrosion resistance, and biocompatibility. An experimental sample of NiTi alloy was subjected to annealing at different temperatures ranging from 350°C to 650°C. The microstructural, thermal and mechanical properties before and after the heat treatment were studied. The influence of annealing heat treatment in low temperatures on the microstructure of Ni53Ti47 was investigated. The results showed that the annealing treatment led to changes in the microstructure morphology. It was noticed that the martensitic transformation temperatures Ms and Af tend to increase with the annealing temperature growth. The R-phase is presented in the specimens considering the range of 350°C to 550°C, with complete solubilization at 650°C. Such changes were accompanied by a gradual decrease in hardness and rise in grain size with the increase of the annealing temperature.
Near-equiatomic NiTi alloys (or Nitinol) exhibit shape memory behavior, superelasticity, high strength, excellent corrosion resistance, and biocompatibility. An experimental sample of NiTi alloy was subjected to annealing at different temperatures ranging from 350°C to 650°C. The microstructural, thermal and mechanical properties before and after the heat treatment were studied. The influence of annealing heat treatment in low temperatures on the microstructure of Ni53Ti47 was investigated. The results showed that the annealing treatment led to changes in the microstructure morphology. It was noticed that the martensitic transformation temperatures Ms and Af tend to increase with the annealing temperature growth. The R-phase is presented in the specimens considering the range of 350°C to 550°C, with complete solubilization at 650°C. Such changes were accompanied by a gradual decrease in hardness and rise in grain size with the increase of the annealing temperature.
Descripción
Organizado y patrocinado por: Federación iberoamericana de Ingeniería Mecánica y 'Universidad de Concepción - Chile. Departamento de Mecánica', FeIbIm – FeIbEM.
Categorías UNESCO
Palabras clave
Ligas com memória de forma (SMA), ligas de NiTi, tratamento térmico, microestrutura, Shape memory alloys (SMA), NiTi alloys, heat treatment, microstructure