Publicación: Soldadura continua por ultrasonidos en termoplásticos reforzados de fibra de carbono
No hay miniatura disponible
Archivos
Fecha
2022
Editor/a
Director/a
Tutor/a
Coordinador/a
Prologuista
Revisor/a
Ilustrador/a
Derechos de acceso
Atribución-NoComercial-SinDerivadas 4.0 Internacional
info:eu-repo/semantics/openAccess
info:eu-repo/semantics/openAccess
Título de la revista
ISSN de la revista
Título del volumen
Editor
['Universidad Nacional de Educación a Distancia (España)', 'Universidad Politécnica de Madrid. Departamento de Ingeniería Mecánica']
Resumen
La soldadura por ultrasonidos (USW) de termoplásticos es un método de unión de bajo coste que elimina el uso de disolventes o adhesivos produciendo un calentamiento localizado en tiempos muy cortos. El proceso de soldadura lo hemos realizado de forma continua. Los materiales que se han van a unir son cintas de CFRTP de pequeño espesor (menos de 0.5 micrómetros) y de matriz semi-cristalina. Se ha podido comprobar que con este proceso es posible obtener uniones con menos de 2% de porosidad y cristalinidad más alta del 20%; son valores muy positivos, teniendo en cuenta que es un proceso continuo
Ultrasonic welding (USW) of thermoplastics is a low-cost joining method that eliminates the use of solvents or adhesives, producing localized heating in a very short time. We have carried out the welding process continuously. The materials joined are CFRTP tapes with a small thickness (less than 0.5 micrometers) and a semi-crystalline matrix. It has been possible to verify how with this process it is possible to obtain joints with less than 2% porosity and crystallinity higher than 20%, which are very positive values, considering that it is a continuous process.
Ultrasonic welding (USW) of thermoplastics is a low-cost joining method that eliminates the use of solvents or adhesives, producing localized heating in a very short time. We have carried out the welding process continuously. The materials joined are CFRTP tapes with a small thickness (less than 0.5 micrometers) and a semi-crystalline matrix. It has been possible to verify how with this process it is possible to obtain joints with less than 2% porosity and crystallinity higher than 20%, which are very positive values, considering that it is a continuous process.
Descripción
Categorías UNESCO
Palabras clave
ultrasonidos, termoplástico, materiales compuestos