Publicación:
Avaliação da Adição de Grafeno na Dureza e Tenacidade à Fratura de WC-10Co

Vista sencilla de ítem
dc.contributor.authordos Santos Rosa, Jhonatan Dantas
dc.contributor.authorRodrigues das Neves, Daniele
dc.contributor.authorFilgueira, Marcello
dc.contributor.authorBertolete, Marcelo
dc.contributor.authorAlves Barbosa, Patrícia
dc.coverage.spatialConcepción, Chile
dc.coverage.temporal2024-10-22
dc.date.accessioned2025-03-11T07:09:22Z
dc.date.available2025-03-11T07:09:22Z
dc.date.issued2024-10-22
dc.descriptionOrganizado y patrocinado por: Federación iberoamericana de Ingeniería Mecánica y Universidad de Concepción - Chile. Departamento de Mecánica, FeIbIm – FeIbEM
dc.description.abstractO metal duro (WC-Co) é um produto da metalurgia do pó que exibe excelente combinação de dureza e tenacidade à fratura. Este trabalho objetiva avaliar a influência da adição de grafeno na densificação, dureza e tenacidade à fratura de WC-10Co. Para tanto, 0,1% em massa de grafeno com poucas camadas (FLG) foi adicionada em mistura de pós ultrafino e fino de WC e Co, respectivamente. As amostras foram sinterizadas por corrente elétrica pulsada (SPS) a 1400ºC, com pressão uniaxial de 40 MPa e atmosfera em baixo vácuo. Foram avaliadas a densidade, a dureza Vickers e a tenacidade à fratura (KIC). Os resultados mostraram pouca influência do grafeno na densificação e na dureza. Todavia, houve aumento estatisticamente significativo de 14,9% no KIC ao comparar com a amostra de referência. Conclui-se que o grafeno tem potencial para a melhoria de propriedades, porém as condições de sinterização precisam ser ajustadas.pt
dc.description.abstractCemented carbide (WC-Co) is a powder metallurgy product that exhibits an excellent combination of hardness and fracture toughness. This work aims to evaluate the influence of graphene addition on the densification, hardness and fracture toughness of WC-10Co. For this purpose, 0.1% by weight of few-layer graphene (FLG) was added to a mixture of ultrafine and fine powders of WC and Co, respectively. The samples were sintered by spark plasma sintering (SPS) at 1400ºC, with uniaxial pressure of 40 MPa and a low vacuum atmosphere. Density, Vickers hardness and fracture toughness (KIC) were evaluated. The results showed little influence of graphene on densification and hardness. However, there was a statistically significant increase of 14.9% in KIC compared to the reference sample. It is concluded that graphene can potentially improve properties, but the sintering conditions need to be adjusted.en
dc.description.versionversión publicada
dc.identifier.citation-
dc.identifier.urihttps://hdl.handle.net/20.500.14468/26219
dc.language.isopt
dc.publisherUniversidad Nacional de Educación a Distancia (España), Universidad de Concepción - Chile. Departamento de Ingeniería Mecánica
dc.relation.centerE.T.S. de Ingenieros Industriales
dc.relation.congressXVI Congreso Iberoamericano de Ingeniería Mecánica. Concepción, Chile, 22-24 de octubre de 2024. CIBIM 2024
dc.relation.departmentMecánica
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/4.0/deed.es
dc.subject33 Ciencias Tecnológicas
dc.subject.keywordsmetal duropt
dc.subject.keywordsgrafenopt
dc.subject.keywordsdureza Vickerspt
dc.subject.keywordstenacidade à fraturapt
dc.subject.keywordscemented carbideen
dc.subject.keywordsgrapheneen
dc.subject.keywordsVickers hardnessen
dc.subject.keywordsfracture toughnessen
dc.titleAvaliação da Adição de Grafeno na Dureza e Tenacidade à Fratura de WC-10Copt
dc.typeactas de congresoes
dc.typeconference proceedingsen
dspace.entity.typePublication
Archivos
Bloque original
Mostrando 1 - 1 de 1
Miniatura
Nombre:
5924_Articulo-Aceptado.pdf
Tamaño:
743.19 KB
Formato:
Adobe Portable Document Format
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
No hay miniatura disponible
Nombre:
license.txt
Tamaño:
3.62 KB
Formato:
Item-specific license agreed to upon submission
Descripción:
Descargar
Colecciones
Actas y comunicaciones de congresos