Publicación: Estudio experimental de las propiedades mecánicas del mortero reforzado con fibras de PET tratadas térmicamente
Cargando...
Fecha
2024-10-22
Editor/a
Director/a
Tutor/a
Coordinador/a
Prologuista
Revisor/a
Ilustrador/a
Derechos de acceso
info:eu-repo/semantics/openAccess
Título de la revista
ISSN de la revista
Título del volumen
Editor
Universidad Nacional de Educación a Distancia (España), Universidad de Concepción - Chile. Departamento de Ingeniería Mecánica
Resumen
El presente trabajo tuvo como objetivo caracterizar el comportamiento mecánico del mortero con adición de fibras de PET tratadas térmicamente. Se utilizaron botellas de PET recicladas cortadas a 35 mm de longitud, y ancho entre 2 a 3 mm. Las fibras se utilizaron sin tratamiento térmico, con tratamiento en agua caliente, microondas y una combinación de estos dos últimos. En los ensayos de flexión, la inclusión de fibras demostró mejoras significativas en la resistencia del 9% al 24% respecto al control, proporcionando un comportamiento más dúctil, una mayor capacidad de contención de grietas y absorción de carga después de la falla. Para los ensayos de compresión, se observó un aumento general en la resistencia, sin embargo, se presentó una disminución en la resistencia de las probetas con fibras de tratamiento de agua caliente.
The aim of this work was to characterize the mechanical behavior of mortar with the addition of heat-treated PET fibers. Recycled PET bottles cut to 35 mm in length and 2 to 3 mm in width were used. The fibers were used without heat treatment, with hot water treatment, microwave treatment, and a combination of the latter two. In the flexural tests, the inclusion of fibers demonstrated significant improvements in strength from 9% to 24% compared to the control, providing more ductile behavior, greater crack containment capacity, and load absorption after failure. For the compression tests, a general increase in strength was observed, however, a decrease in the strength of the specimens with hot water treated fibers was presented.
The aim of this work was to characterize the mechanical behavior of mortar with the addition of heat-treated PET fibers. Recycled PET bottles cut to 35 mm in length and 2 to 3 mm in width were used. The fibers were used without heat treatment, with hot water treatment, microwave treatment, and a combination of the latter two. In the flexural tests, the inclusion of fibers demonstrated significant improvements in strength from 9% to 24% compared to the control, providing more ductile behavior, greater crack containment capacity, and load absorption after failure. For the compression tests, a general increase in strength was observed, however, a decrease in the strength of the specimens with hot water treated fibers was presented.
Descripción
Organizado y patrocinado por: Federación iberoamericana de Ingeniería Mecánica y 'Universidad de Concepción - Chile. Departamento de Mecánica', FeIbIm – FeIbEM
Categorías UNESCO
Palabras clave
mortero, PET, tratamiento térmico, propiedades mecánicas, mortar, PET, heat treatment, mechanical properties