Estudo comparativo da resistência à corrosão de metais duros WC NiMo e WC-Co

Alves Nery Balbino, Nadia, Otoni Corrêa, Edmilson, Roque Huanca, Danilo y Amaury de Freitas Matos, Flávio(2022) .Estudo comparativo da resistência à corrosão de metais duros WC NiMo e WC-Co. XV Congreso Iberoamericano de Ingeniería Mecánica.En: Universidad Politécnica de Madrid. (2022-11-22)

Ficheros (Some files may be inaccessible until you login with your e-spacio credentials)
Nombre Descripción Tipo MIME Size
Abs_294_185631.docx Estudo comparativo da resistência à corrosão Click to show the corresponding preview/stream application/vnd.openxmlf... 5.48MB

Título de la Conferencia XV Congreso Iberoamericano de Ingeniería Mecánica
Fecha de inicio de la Conferencia 2022-11-22
Fecha fín de la Conferencia 2022-11-24
Lugar de la Conferencia Universidad Politécnica de Madrid
Fecha de presentación de la Ponencia 2022
Titulo Estudo comparativo da resistência à corrosão de metais duros WC NiMo e WC-Co
Autor(es) Alves Nery Balbino, Nadia
Otoni Corrêa, Edmilson
Roque Huanca, Danilo
Amaury de Freitas Matos, Flávio
Materia(s) Ingeniería Mecánica
Resumen Metais duros com ligante de cobalto dominam o mercado, pois apresentam boas propriedades mecânicas. Entretanto, sua substituição é motivada pela baixa resistência à corrosão, alto custo e toxicidade. O níquel é um substituto promissor, porém, resulta em propriedades mecânicas inferiores. Para aprimorar essas propriedades, adição de elementos de liga, como molibdênio, tem sido estudada. O objetivo deste trabalho foi avaliar e comparar a resistência à corrosão dos metais duros WC-Co e WC-NiMo. A resistência à corrosão, em solução NaCl 3,5% em peso, foi estudada pelas técnicas de potencial de circuito aberto, polarização potenciodinâmica linear e espectroscopia de impedância eletroquímica. As amostras foram caracterizadas antes e após os ensaios. O metal duro WC-NiMo apresentou microestrutura semelhante ao WC-Co, porém, observaram-se poros e ilhas de ligante. Os ensaios de corrosão obtiveram resultados promissores, o metal duro WC-NiMo apresentou resistência à corrosão superior e maior capacidade de passivação do que o WC Co.
Abstract Cobalt is the binder that dominates the market due to better mechanical properties. However, due to the low corrosion resistance, high cost and toxicity, an alternative binder phase has been researched. Nickel is a promising candidate but, the mechanical properties of WC Ni are inferior to those of WC-Co. To improve these properties, the addition of alloying elements, such as molybdenum, has been studied. The aim of this work was to evaluate and compare the corrosion resistance of WC-Co and WC NiMo. The corrosion resistance of the cemented carbides was investigated by open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy, in a 3.5wt.% NaCl solution. The sintered alloys were characterized before and after corrosive tests. The WC-NiMo showed microstructures similar to those of WC-Co, however, pores and binder islands were observed. The corrosion tests had promising results, the WC-NiMo showed superior corrosion resistance and higher passivation capacity than WC-Co.
Palabra clave metal duro WC-Ni
resistência a corrosão
polarização potenciodinâmica linear
espectroscopia de impedância eletroquímica
Editor(es) Universidad Nacional de Educación a Distancia (España)
Universidad Politécnica de Madrid. Departamento de Ingeniería Mecánica
Fecha 2022
Formato application/ms-word
Identificador bibliuned:congresoCIBIM-2022UPMEspana-Nalves
https://doi.org/10.5944/bicim2022.208
http://e-spacio.uned.es/fez/view/bibliuned:congresoCIBIM-2022UPMEspana-Nalves
Idioma por
Versión de la publicación publishedVersion
Nivel de acceso y licencia http://creativecommons.org/licenses/by-nc-nd/4.0
info:eu-repo/semantics/openAccess
Tipo de recurso conferenceObject
Tipo de acceso publishedVersion

 
Versiones
Versión Tipo de filtro
Contador de citas: Google Scholar Search Google Scholar
Estadísticas de acceso: 180 Visitas, 37 Descargas  -  Estadísticas en detalle
Creado: Wed, 18 Jan 2023, 22:07:54 CET